Polyethylene joint wrap tape

System description:

 

The XUNDA-T300 series is Cold applied tape coating system for anti corrosion of field joints,fittings, and specifically pipeing. The adhesive is a key in ground performance characteristic coupled with the low and high density polyethylene backing. 

 

The Polyethylene Joint wrap tape shall be applied by hand or with a wrapping machine.

 

Structure:

The specification of the tape consists of two layers, adhesive layer and film backing

Adhesive: butyl rubber 

Film backing: Special blend of stabilized polyethylene

 

Features:

Heavy duty adhesive

Resistant to UV

Can be applied over a wide temperature range 

Good conformability and consistent uniform thickness

Easily applied with no special equipment

Conformable to irregular shapes.

Meets ASTM D 1000 Standard

Cold applied

 

Physical Properties:

Physical Properties	Test Method	Typical Value
		English	Metric
Total thickness	ASTM D 1000	40.0 mil	1.00 mm
Backing thickness	ASTM D 1000	14.0 mil	0.35 mm
Adhesive thickness	ASTM D 1000	26.0 mil	0.65 mm
Width	-	2’’- 32 ‘’	50 -800 mm
Length	-	100’ -800 ‘	30 -240 m
Backing colour	-	Black,Yellow,Gray or orthers
Tensile strength	ASTM D 1000	28 lbs/in	49 N/ cm
Elongation	ASTM D 1000	450 %
Peel Adhesion to primed steel pipe	ASTM D 1000	339 oz/in	37 N/cm
Cathodic Disbandment	ASTM G8	0.25 in radius 6.4 mm
Dielectric Strength	ASTM D 149	42 Kv
Volume Resistivity	ASTM D 257	2.5x1012 ohm.cm
Water Absorptivity	ASTM D 570	0.1%
Water Vapor Transmission Rate （24h）	ASTM F1249	0.01g/100sq in/24h	0.1g/100sq mm/24h
Application Temperature		14℉-140℉	-10 ℃ - 60 ℃
Max Service Temperature		-40℉-176℉	- 40 ℃ - 80℃